| Customization: | Available |
|---|---|
| Material: | PE |
| Kind: | Engineering Plastic Sheet |
|
Still deciding? Get samples of US$ 50/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Heavy Duty Lightweight Polyethylene Portable Crane Stabilizer Jack Pads supply a range of lightweight and long-lasting spreader plates that offer stable support when operating cranes, aerial work platforms and mobile plant. Made from high quality, heavy duty UHMW polyethylene, our range of outrigger pads offer protection against water, corrosion and splintering - a huge advancement over the more traditional wooden and steel alternatives.
- Guaranteed Unbreakable
- Made in the China
- Leading time within 15 days
Here, any size and color of Crane Outrigger Pad are aviable with us
Products Description
Xinxing Heavy Duty Lightweight Polyethylene Portable Crane Stabilizer Jack Pads provide a super strong, rigid and easy to use foundation for a wide variety of outrigger enabled equipment. Constructed of engineered thermoplastic material, with a crush rating up to 750 psi and maximum allowable load ratings up to 300,000 lbs., Xinxing Heavy Duty Lightweight Polyethylene Portable Crane Stabilizer Jack Pads deliver the strength, stiffness and reliability you can trust.
1. Different surface
A Smooth Surface B Circle in Middle C Rhombus pattern in surface D Anti-slip Surface
2. Handle
A : With nylon rope and rubber sleeve B : With hole holder on top C : With Steel Chain
3. Shape
A : Square shape B:Round shape
--Highest abrasion resistance of any polymer, 6 times more abrasion resistant than steel
--Do not absorb moisture and will not swell up over time due to exposure outdoors.
--Good impact intensity,Do not lose their impact strength over time.
--Good breaking elongation,so they will bend but not break under extreme loads.
--Non-stick surface, easy to clean.
--Corrosion and chemical resistant.
--Noise- absorption, Vibration-absorption
--Super compression strength
--15 Percent the weight of steel pads and easier to handle
--Compressive loads up to one million pounds
--Up to 15,000 pounds per square foot
--Non-Conductive
--Non-Toxic and smell
Applications
Xinxing Heavy Duty Lightweight Polyethylene Portable Crane Stabilizer Jack Pads put under the support-leg Truck Crane, Crawler Crane, Rough Crane, Boom Pump, Concrete Pump, Fire Truck, Utility Truck, Tree Trimmer, Any type of Aerial Equipment and so on, for making the machine work safely.
Xinxing Heavy Duty Lightweight Polyethylene Portable Crane Stabilizer Jack Pads are available in three categories; Medium Duty (1.0″ thick), Heavy Duty (2.0″ thick) and Super Duty (3.0″ and 4.0″ thick) and are designed for equipment typically up to 100 tons in capacity.
As the thickness of a Heavy Duty Lightweight Polyethylene Portable Crane Stabilizer Jack Pads increases it has a greater ability to distribute higher loads over the ground.
The size and thickness of the Heavy Duty Lightweight Polyethylene Portable Crane Stabilizer Jack Pads you need depends on your equipment type/specifications and the soil bearing capacity.
Size & Load Capacity
| Dimensions(mm) | Weight(kg) | Vertical Jack Capacity (tonne) | 45° Load(tonnes) |
| 400*400*40 | 6.14 | 30 | 18 |
| 500*500*25 | 6.00 | 27 | 16 |
| 500*500*50 | 12.00 | 35 | 22 |
| 600*600*50 | 17.28 | 35 | 22 |
| 800*800*60 | 36.86 | 45 | 25 |
| 1000*1000*100 | 96.00 | 80 | 40 |
Techinal Data Sheet
| Property: | Test Method (Standard) | Ticona GUI4152 | Ticona GUI4150,4120 | Unit |
| Molecular weight | 3-5 million | 3-5 million | ||
| Density | ISO 1183-1:2012/DIN53479 | 0.92-0.98 | 0.93-0.98 | g/cm³ |
| Compression strength | ISO 604:2002 | ≥30 | ≥32 | Mpa |
| Tensile strength | ISO527-2:2012 | ≥20 | ≥22 | Mpa |
| Elongation at break | ISO527-2:2012 | ≥300 | ≥300 | % |
| Dynamic Friction coefficient | ASTM D 1894/GB10006-88 | ≤0.20 | ≤0.18 | |
| Dynamic Friction coefficient | ASTM D 1894/GB10006-88 | ≤0.20 | ≤0.18 | |
| Notched impact strength (Charpy) | ISO179-1:2010/GB/T 1043.1-2008 | ≥100 | ≥100 | kJ/m2 |
| Abrasion wear index | ES-X60210-2008 | ≤30 | ≤30 | mg |
| Vicat softing point | ISO306:2004 | ≥80 | ≥80 | °C |
| Hardness shore-D | ISO 868:2003 | 60-65 | 61-66 | D |
){kind=link}