Marine Fender Front Panel Boat Fender Panel

• After-sales Service: After Servie
• Warranty: 2years
• Material: UHMWPE
• Shape: Available to Customers
• Structure: Solid
• Size: 0.7*1.5~1.0*1.5m
• Model NO.: XX-012
• Advantage: Anti-Corrosion
• Customized: Accept Customized Products
• Transport Package: Pallet, by Sea
• Specification: 800*800*50mm, 745*745*50mm etc
• Trademark: Xinxing
• Origin: Dezhou, China
• HS Code: 3920109090
• Production Capacity: 5000000 Tons/Year

Product Description

Marine Fender Front Panel, Boat Fender Panel




Introduction:
Ultra-high molecular weight polyethylene(UHMWPE) dock fender could avoid the impact damage between ships and dock. Because of the high impact resistance performance, UHMWPE dock fender instead of the traditional steel ones is widely used in ports and docks at home and abroad.
Our UHMW PE-1000 marine fenders are made from virgin uhmwpe material, which is much superior to wood and rubber in building marine constructions or coastal protective structures. UHMW PE-1000 marine fenders allow vessels to glide easily along the surface, protecting hulls and dock structures. Impervious to marine bore worms with minimum cleaning.


Feature:
1.Highest abrasion resistance of any polymer, 6 times more wear resistance than steel
2.Anti-weather & anti-aging
3.Self-lubricating and very low coefficient of friction
4.Excellent chemical & corrosion resistant; Stable chemical property and can endure the corrosion of all kind of corrosive medium and organic solvent in certain range of temperature and humidity.
5.Superior impact resistant, noise-absorption and vibration-absorption;
Low water absorption <0.01% water absorption and not affected by temperature.
6.Temperature range: -269ºC~+85ºC;
Very high resistance to cold, doesn't become fragile even under -180ºC.
7.High tensile strength
8.Non-toxic and no odor
9.UV resistance and long service life
10.Good performance in resisting environment stress crack

Technical data:

Property	Unit	Value
Density	g/cm3	0.93-0.96
Average molecular weight	g/mol	3million- 10 million
Tensile strength (23°C in air)	MPa	22
Breaking strength	MPa	42
Tensile strain at break	%	600
Charpy impact strength (notched)	mJ/mm2	No break
Ball indentation hardness	N/mm2	42
Shore hardness	--	65-70
Abrasion	%	70-80, steel = 100
Static Friction Coefficient	--	≤0.16
Kinetic Friction Coefficient	--	≤0.10
Water Absorption	--	NIL
Elongation at break at 23°C	%	≥300
Temperature Resistance	°C	-269 to +85
Melt Temperature	°C	130-140

Application:
1.Harbour instruction :
Wear pad to replace wood and rubber
protective quay wall
2.truck dock
fenders for dock plate protection
3.Piling
Fenders
Wear plate and slides
4.floating dock
wear plate where dock meets pillage
fenders
Slides


Key words:
UHMW-PE wear plastic plate polyethylene dock fender panel / high impact uhmwpe marine fender pad